Dekalin DEKAsyl MS 5 sylil modified polymer power glue 290 mL (white)
Dekalin DEKAsyl MS 5 sylil modified polymer power glue 290 mL (white)

Dekalin DEKAsyl MS 5 sylil modified polymer power glue 290 mL (white)

Article no.: 107940
Manufacturer: DEKALIN

Offer is exclusively for commercial customers. Prices are only visible after login.

  • Product description

DEKAsyl MS-5 is a high-quality power adhesive with a high initial strength which can be used in the entire vehicle construction.
The areas of use and application are diverse and can be extended as required.

Colour: White
Content: 290 ml
Packaging: Cartridge

Fields of application:

Bonding of, among others:

- Metal frames
- corner profiles
- Structural bonding of polyester parts
- climate boxes
- solar installations
- SAT systems
- Frame and wheel covers
- and much more

Proper application:

DEKAsyl MS-5 can be easily applied with a hand or air pressure gun. For sealing, Dekasyl MS-5 should be applied within 12 minutes (at 20°C/50 % rel. humidity) with a
previously dipped in a mild soap solution, or smoothened with a spatula or putty knife.
Avoid penetration of the side solution between the joint sides and the sealant, as this will lead to a loss of adhesion.
this will lead to a loss of adhesion. For bonding, the substrates must be bonded within 15 minutes (at
20°C/50% rel. humidity) after application of Dekasyl MS-5. The higher the temperature
the shorter the working time! In general, an adhesive layer of 2 mm is recommended if similar
materials (with similar strength) are to be bonded. The greater the difference in thermal expansion, the thicker the adhesive layer should be. At a temperature of 20°C and a relative humidity of 50%, Dekasyl MS-5 can already be
can be overpainted with most industrial paints after only 10 minutes. The best possible adhesion of
paint coats is achieved if the paint is applied 4 hours after application of Dekasyl MS-5. Clean tools or remove uncured residues of Dekasyl MS-5 with a clean, colourless cloth soaked in acetone or MEK (it is recommended to check beforehand if the
Surface is affected by this cleaner).

Technical data:

Base material: MS polymer
Curing/sealing: moisture

Specific density: approx. 1.4 kg/litre
Skin forming time (20°C/50% rel. LF): approx. 12 minutes

Open time (20°C/50% rel. LF): less than 15 minutes
Curing time after 24 h (20°C/50% rel. LF): approx. 4 mm

Shore A hardness (DIN 53505): approx. 55
Volume change (DIN 52451): less than 3%.

Adhesion (Physical Rheometer MC100): approx.700 Pa
(measure for the max. not cured adhesive quantity which can be applied per m² without running down)

Tensile stress (100%) (DIN 53504/ISO 37): approx. 1.7 MPa
Tensile stress at break (DIN 53504/ISO 37): approx. 2.8 MPa

Elongation at break (DIN 53504/ISO 27): approx. 210
Shear stress (DIN 53283/ASTM D1002): approx. 2.5 MPa

Tear strength (DIN 53515/ISO 34): approx. 14 N/mm
Solvent content:0%

Isocyanate content:0%
Temperature resistance : -40°C to +120°C

Application temperature : +5°C to +35°C
UV and weather resistance: excellent